The hot dipping process consists of passing the steel through a bath of molten zinc, while the electro-galvanizing process consists of the application of zinc through electrolytic disposition. The result is a layer of zinc tightly adhering to the base metal through an iron-zinc bonding layer. Our hot dipped galvanized products are manufactured to ASTM A653 specifications.
| Gauge No.
|
| lbs. po sq. ft. | |
|
|
|
| |
| 10 | .1382 | .1472 .1292 | 5.78125 |
| 11 | .1233 | .1323 .1143 | 5.15625 |
| 12 | .1084 | .1174 .0994 | 4.53125 |
| 13 | .0934 | .1014 .0854 | 3.90625 |
| 14 | .0785 | .0865 .0705 | 3.28125 |
| 15 | .0710 | .0770 .0650 | 2.96875 |
| 16 | .0635 | .0695 .0575 | 2.65625 |
| 17 | .0575 | .0625 .0525 | 2.40625 |
| 18 | .0516 | .0566 .0466 | 2.15625 |
| 19 | .0456 | .0506 .0406 | 1.90625 |
| 20 | .0396 | .0436 .0356 | 1.65625 |
| 21 | .0366 | .0406 .0326 | 1.53125 |
| 22 | .0336 | .0376 .0296 | 1.40625 |
| 23 | .0306 | .0346 .0266 | 1.28125 |
| 24 | .0276 | .0316 .0236 | 1.15625 |
| 25 | .0247 | .0287 .0207 | 1.03125 |
| 26 | .0217 | .0247 .0187 | .90625 |
| 27 | .0202 | .0232 .0172 | .84375 |
| 28 | .0187 | .0217 .0157 | .78125 |
| 29 | .0172 | .0202 .0142 | .71875 |
| 30 | .0157 | .0187 .0217 | .65625 |
Pocinčani čelik je vruće-obložen metal koji kupcima pruža bolju otpornost na korozivna okruženja.
To create galvanized steel, cold rolled steel is submerged into a molten zinc bath, known as the hot-dip process (galvanization can also be achieved through continuous galvanizing). When the material is removed from the zinc bath and cooled a reaction to the oxygen in the air occurs. The reaction causes the zinc coating to become part of the steel creating the well-recognized spangled finish.