Hot Forming
Working temperatures of 1652 – 2102°F (900 – 1150°C) are recommended for hot working processes. Do not work this alloy below 1742°F (950°C). If the final forming temperature falls below this threshold, a solution anneal of 1976 – 2156°F (1080 – 1180°C) is necessary. Rapid quenching is required.
Machining
The cold work hardening rate of Alloy 317L makes it less machinable than 410 stainless steel. The table below provides relevant machining data.
Mechanical Properties of 317/317L Stainless Steel Plate
| Yield Strengtd 0.2% Offset | Ultimate Tensile Strength | Elongation in 2 in. | Hardness | ||
| psi (min.) | (MPa) | psi (min.) | (MPa) | % (min.) | (max.) |
| 30,000 | 205 | 75,000 | 515 | 40 | 95 Rockwell B |